Mohala oa Tlhahiso ea Carbon Fiber Precursor
Tlhaloso
Mokhoa oa tlhahiso ea carbon fiber precursor o amohelang Dimethyl Sulfoxide(DMSO) e le solvent, Acrylonitrile(AN) e le monomer ea pele, Itaconic Acid e le monoma ea bobeli, AIBN e le mothehi oa ho ba le binary copolymerization, le jet e omileng e ohlang metsi. ke khetho e holimo eo ho lumellanoeng ka eona har'a litsebi tsa carbon fiber.
Lintlha tsa Tech:
Che. | Ntho | Yuniti | Litlhaloso | Litlhaloso |
1 | Linear Density | dtex | 1.15 | |
2 | Matla a tšepe | CN/dtex | ≥4.0 | |
3 | Elongation | % | 12±2 | |
4 | Dimethyl Sulfoxide (DMSO) Content | % | <0.03 | |
5 | Likahare tsa Oli | % | 0.5-0.1 | |
6 | Felisa Sekhahla | % | <3 | |
7 | Mongobo Hape | % | ≤1 | |
8 | Ponahalo | Ha ho na Filament e Hlahang e Senyehileng |
Tshebetso:
Tlhophiso e tala —→ Monomer Mixture —→ Copolymerization —→ Primary Filtration —→ Monomer Removal —→ Secondary Filtration —→ Mixed Batch Neutralization —→ Tertiary Filtration —→ Storage —→ Defoam —→ Spinning —→ spin bath (Primary) —→ spin bath (Bobeli) —→ spin bath (Tertiary) —→ Clean —→ Hot Stretching —→ Ho Oling —→ Ho omisa —→ Ho Otlolla Mouoane —→ Ho Seta Mocheso —→ Antistatic Treatment —→ Precursor Wining
Che. | Ntho | Yuniti | Litlhaloso | Litlhaloso |
1 | Linear Density | dtex | 1.15 | |
2 | Matla a tšepe | CN/dtex | ≥4.0 | |
3 | Elongation | % | 12±2 | |
4 | Dimethyl Sulfoxide (DMSO) Content | % | <0.03 | |
5 | Likahare tsa Oli | % | 0.5-0.1 | |
6 | Felisa Sekhahla | % | <3 | |
7 | Mongobo Hape | % | ≤1 | |
8 | Ponahalo | Ha ho na Filament e Hlahang e Senyehileng |
Raw Tokisetso ea Lintho —→ Motsoako oa Monomer —→ Copolymerization —→ Primary Filtration —→ Monomer Removal —→ Second Filtration —→ Mixed Batch Neutralization —→ Tertiary Filtration —→ Storage —→ Defoam —→ Spinning —→ spin bath (Primary) —→ spin bath (Bobeli) —→ spin bath (Tertiary) —→ Clean —→ Hot Stretching —→ Ho Oling —→ Ho omisa —→ Ho Otlolla Mouoane —→ Ho Seta Mocheso —→ Antistatic Treatment —→ Precursor Wining